| Customization: | Available |
|---|---|
| Type: | Rigid Circuit Board |
| Dielectric: | CEM-3 |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| PCB Material: | Glass microfiber reinforced PTFE composites |
| Designation: | RT/duroid 5880 |
| Dielectric constant: | 2.2 ±0.02 (process) |
| 2.2 (design) | |
| Layer count: | 2 Layer, Multilayer, Hybrid type (Mixed) |
| Copper weight: | 0.5oz (17 µm), 1oz (35µm), 2oz (70µm) |
| PCB thickness: | 10mil (0.254mm), 20mil (0.508mm) |
| 31mil (0.787mm), 62mil (1.575mm) | |
| PCB size: | ≤400mm X 500mm |
| Solder mask: | Green, Black, Blue, Yellow, Red etc. |
| Surface finish: | Bare copper, HASL, ENIG, OSP, etc.. |
| RT/duroid 5880 Typical Value | ||||||
| Property | RT/duroid 5880 | Direction | Units | Condition | Test Method | |
| Dielectric Constant,εProcess | 2.20 2.20±0.02 spec. |
Z | N/A | C24/23/50 C24/23/50 |
1 MHz IPC-TM-650 2.5.5.3 10 GHz IPC-TM 2.5.5.5 |
|
| Dielectric Constant,εDesign | 2.2 | Z | N/A | 8GHz to 40 GHz | Differential Phase Length Method | |
| Dissipation Factor,tanδ | 0.0004 0.0009 |
Z | N/A | C24/23/50 C24/23/50 |
1 MHz IPC-TM-650 2.5.5.3 10 GHz IPC-TM 2.5.5.5 |
|
| Thermal Coefficient of ε | -125 | Z | ppm/ºC | -50ºCto 150ºC | IPC-TM-650 2.5.5.5 | |
| Volume Resistivity | 2 x 107 | Z | Mohm cm | C/96/35/90 | ASTM D 257 | |
| Surface Resistivity | 3 x 107 | Z | Mohm | C/96/35/90 | ASTM D 257 | |
| Specific Heat | 0.96(0.23) | N/A | j/g/k (cal/g/c) |
N/A | Calculated | |
| Tensile Modulus | Test at 23ºC | Test at 100ºC | N/A | MPa(kpsi) | A | ASTM D 638 |
| 1070(156) | 450(65) | X | ||||
| 860(125) | 380(55) | Y | ||||
| Ultimate Stress | 29(4.2) | 20(2.9) | X | |||
| 27(3.9) | 18(2.6) | Y | ||||
| Ultimate Strain | 6 | 7.2 | X | % | ||
| 4.9 | 5.8 | Y | ||||
| Compressive Modulus | 710(103) | 500(73) | X | MPa(kpsi) | A | ASTM D 695 |
| 710(103) | 500(73) | Y | ||||
| 940(136) | 670(97) | Z | ||||
| Ultimate Stress | 27(3.9) | 22(3.2) | X | |||
| 29(5.3) | 21(3.1) | Y | ||||
| 52(7.5) | 43(6.3) | Z | ||||
| Ultimate Strain | 8.5 | 8.4 | X | % | ||
| 7.7 | 7.8 | Y | ||||
| 12.5 | 17.6 | Z | ||||
| Moisture Absorption | 0.02 | N/A | % | 0.62"(1.6mm) D48/50 | ASTM D 570 | |
| Thermal Conductivity | 0.2 | Z | W/m/k | 80ºC | ASTM C 518 | |
| Coefficient of Thermal Expansion | 31 48 237 |
X Y Z |
ppm/ºC | 0-100ºC | IPC-TM-650 2.4.41 | |
| Td | 500 | N/A | ºC TGA | N/A | ASTM D 3850 | |
| Density | 2.2 | N/A | gm/cm3 | N/A | ASTM D 792 | |
| Copper Peel | 31.2(5.5) | N/A | Pli(N/mm) | 1oz(35mm)EDC foil after solder float |
IPC-TM-650 2.4.8 | |
| Flammability | V-0 | N/A | N/A | N/A | UL 94 | |
| Lead-free Process Compatible | Yes | N/A | N/A | N/A | N/A | |